沙伯基础防火PPE/PS NORYL SE100HX

Mechanical PropertiesMetricEnglishComments

Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D 792
Water Absorption	0.060 % @Time 86400 sec	0.060 % @Time 24.0 hour	ASTM D 570
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	on Tensile Bar; SABIC Method
Tensile Strength at Break	46.0 MPa	6670 psi	Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield	61.0 MPa	8850 psi	Type I, 50 mm/min; ASTM D 638
Elongation at Break	21 %	21 %	Type I, 50 mm/min; ASTM D 638
Elongation at Yield	7.5 %	7.5 %	Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength	89.0 MPa	12900 psi	2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus	2.34 GPa	339 ksi	2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched	0.900 J/cm @Temperature -30.0 °C	1.69 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	2.29 J/cm @Temperature 23.0 °C	4.29 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Instrumented Impact Energy at Peak	3.00 J @Temperature -30.0 °C	2.21 ft-lb @Temperature -22.0 °F	ASTM D 3763
	31.0 J @Temperature 23.0 °C	22.9 ft-lb @Temperature 73.4 °F	ASTM D 3763