经销瑞士EMS增韧级PA12 Grilamid L25 W10 HX
Density | 1.01 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 1.2 | % | ||
Flow | 0.80 | |||
Water Absorption | ISO 62 | |||
Saturation, 23°C | 1.5 | |||
Equilibrium, 23°C, 50% RH | 0.70 | |||
| Hardness | Dry | Conditioned | Unit | Test Method |
Shore Hardness (Shore D, 15 sec) | 67 | ISO 868 |
| Mechanical | Dry | |||
Tensile Modulus | 600 | MPa | ISO 527-2 | |
Tensile Stress | ISO 527-2 | |||
Yield | 35.0 | |||
Break | 40.0 | |||
Tensile Strain | 15 | > 50 | ||
Nominal Tensile Strain at Break | ISO 527-2 | |||
| Impact | Dry | |||
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 7.0 | kJ/m² | ||
23°C | 95 | |||
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | No Break | |||
23°C |
| Thermal | Dry | |||
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B | |
1.8 MPa, Unannealed | 45.0 | ISO 75-2/A | ||
Continuous Use Temperature | ||||
-- 2 | 80.0 to 120 | ISO 2578 | ||
-- 3 | 150 | Internal Method | ||
Melting Temperature 4 | 175 | ISO 11357-3 | ||
CLTE | ISO 11359-2 | |||
Flow | 1.3E-4 | cm/cm/°C | ||
Transverse | 1.6E-4 |
| Electrical | Dry | ||
Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
Electric Strength | 32 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | V | IEC 60112 | |
| Flammability | Dry | ||
Flammability Classification (0.8 mm) | HB | IEC 60695-11-10, -20 |