德国巴斯夫PA66 Ultramid A3EG3玻纤增强15%
德国巴斯夫PA66 Ultramid A3EG3玻纤增强15%
Density / Specific Gravity | 1.24 | -- | g/cm³ | ASTM D792, ISO 1183 |
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg) | 70 | cm³/10min | ISO 1133 | |
Molding Shrinkage - Flow (3.18 mm) | 0.55 | % | ||
Water Absorption | ||||
Saturation | 7.0 | ASTM D570 | ||
Saturation, 23°C | ISO 62 | |||
Equilibrium, 50% RH | 2.2 | ASTM D570 | ||
Equilibrium, 23°C, 50% RH | ISO 62 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 6000 | 4500 | MPa | ISO 527-2 |
Tensile Strength | ||||
Break, 23°C | 114 | ASTM D638 | ||
Break, -40°C | 156 | ISO 527-2 | ||
Break, 23°C | 130 | 85.0 | ISO 527-2 | |
Tensile Elongation | 3.0 | 2.6 | 10 | ISO 527-2 |
Flexural Modulus | ||||
23°C | 5170 | ASTM D790 | ||
23°C | 5200 | 4000 | ISO 178 | |
Flexural Stress (23°C) | 180 | 125 | ISO 178 | |
Impact | Dry | |||
Charpy Notched Impact Strength | ISO 179 | |||
-30°C | kJ/m² | |||
23°C | 8.0 | 11 | ||
Charpy Unnotched Impact Strength | 43 | 45 | ||
Notched Izod Impact | ||||
-40°C | 53 | J/m | ASTM D256 | |
23°C | 59 | 5.5 | 14 | ISO 180 |