NORYL™ SE100X resin 物性表基本信息黄卡编号E207780-228588添加剂阻燃性特性Chlorine Free无溴阻燃性加工方法注塑成型物理性能额定值单位制测试方法比重1.10g/cm³ASTM D792收缩率内部方法    流动 : 3.20 mm0.50 到 0.70%内部方法    横向流动 10.50 到 0.70%内部方法室外适用性f1UL 746C机械性能额定值单位制测试方法抗张强度 2ASTM D638    屈服57.9MPaASTM D638    断裂46.9MPaASTM D638伸长率 3ASTM D638    屈服6.5%ASTM D638    断裂25%ASTM D638弯曲模量 4(100 mm 跨距)2310MPaASTM D790弯曲强度 5(屈服, 100 mm 跨距)82.7MPaASTM D790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度ASTM D256    -30°C91J/mASTM D256    23°C260J/mASTM D256装有测量仪表的落镖冲击ASTM D3763    -30°C, Energy at Peak Load16.3JASTM D3763    23°C, Energy at Peak Load40.7JASTM D3763热性能额定值单位制测试方法载荷下热变形温度ASTM D648    0.45 MPa, 未退火, 6.40 mm102°CASTM D648    1.8 MPa, 未退火, 6.40 mm92.8°CASTM D648RTI Elec95.0°CUL 746RTI Imp80.0°CUL 746RTI95.0°CUL 746电气性能额定值单位制测试方法表面电阻率> 1.0E+15ohmsASTM D257体积电阻率3.1E+16ohms·cmASTM D257介电强度 (3.20 mm, in Oil)18kV/mmASTM D149介电常数ASTM D150    50 Hz2.66ASTM D150    60 Hz2.66ASTM D150    1 MHz2.57ASTM D150耗散因数ASTM D150    50 Hz6.0E-3ASTM D150    60 Hz6.0E-3ASTM D150    1 MHz2.6E-3ASTM D150耐电弧性 6PLC 7ASTM D495相比耐漏电起痕指数(CTI)PLC 1UL 746高电压电弧起痕速率 (HVTR)PLC 4UL 746可燃性额定值单位制测试方法UL 阻燃等级UL 94    1.47 mmV-1UL 94    5.99 mmV-0UL 94极限氧指数33%ASTM D2863Radiant Panel Listing (UL)YES注射额定值单位制干燥温度76.7 到 82.2°C干燥时间3.0 到 4.0hr干燥时间，大8.0hr建议的水分含量0.020%建议注射量30 到 70%料筒后部温度216 到 266°C料筒中部温度227 到 271°C料筒前部温度238 到 277°C射嘴温度249 到 277°C加工（熔体）温度249 到 277°C模具温度54.4 到 76.7°C背压0.345 到 0.689MPa螺杆转速20 到 100rpm排气孔深度0.038 到 0.051mm