Physical PropertiesMetricEnglishCommentsMechanical PropertiesMetricEnglishCommentsElectrical PropertiesMetricEnglishCommentsThermal PropertiesMetricEnglishComments

Density	1.65 g/cc	0.0596 lb/in³	ISO 1183
Water Absorption	0.070 % @Time 86400 sec	0.070 % @Time 24.0 hour	In 23°C water; ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	80x80x3mmt; Toray Method
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	80x80x3mmt; Toray Method
Tensile Strength	105 MPa	15200 psi	ISO 527-1,2
Elongation at Break	2.5 %	2.5 %	ISO 527-1,2
Tensile Modulus	9.80 GPa	1420 ksi	ISO 527-1,2
Flexural Strength	170 MPa	24700 psi	ISO 178
Flexural Modulus	9.20 GPa	1330 ksi	ISO 178
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	V-Notched; ISO 179
Volume Resistivity	6.00e+16 ohm-cm	6.00e+16 ohm-cm	IEC 60093
Dielectric Constant	3.7 @Frequency 1000 Hz	3.7 @Frequency 1000 Hz	60% RH; IEC 60250
	4.0 @Frequency 5000 Hz	4.0 @Frequency 5000 Hz	60% RH; IEC 60250
Dielectric Strength	19.0 kV/mm	483 kV/in	IEC 60243-1
Dissipation Factor	0.0020 @Frequency 5000 Hz	0.0020 @Frequency 5000 Hz	60% RH; IEC 60250
	0.020 @Frequency 1000 Hz	0.020 @Frequency 1000 Hz	60% RH; IEC 60250
Arc Resistance	125 sec	125 sec	W electrode; IEC 60950
CTE, linear, Parallel to Flow	37.0 µm/m-°C @Temperature -30.0 - 100 °C	20.6 µin/in-°F @Temperature -22.0 - 212 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	218 °C	424 °F	ISO 75-1,2
Deflection Temperature at 1.8 MPa (264 psi)	194 °C	381 °F	ISO 75-1,2
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in