Physical PropertiesMetricEnglishCommentsMechanical PropertiesMetricEnglishCommentsElectrical PropertiesMetricEnglishCommentsThermal PropertiesMetricEnglishComments

Density	1.31 g/cc	0.0473 lb/in³	ISO 1183
Water Absorption	0.080 % @Time 86400 sec	0.080 % @Time 24.0 hour	In 23°C water; ISO 62
Linear Mold Shrinkage, Flow	0.017 cm/cm	0.017 in/in	80x80x3mmt; Toray Method
Linear Mold Shrinkage, Transverse	0.023 cm/cm	0.023 in/in	80x80x3mmt; Toray Method
Hardness, Rockwell M	77	77	ISO 2039-2
Tensile Strength	55.0 MPa	7980 psi	ISO 527-1,2
Elongation at Break	10 %	10 %	ISO 527-1,2
Tensile Modulus	2.70 GPa	392 ksi	ISO 527-1,2
Flexural Strength	85.0 MPa	12300 psi	ISO 178
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Charpy Impact Unnotched	15.5 J/cm² @Temperature 23.0 °C	73.8 ft-lb/in² @Temperature 73.4 °F	ISO 179
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	V-Notched; ISO 179
Coefficient of Friction	0.13	0.13	Vs Metal. Without lubrication; Suzuki Method
	0.17	0.17	Vs Metal
Volume Resistivity	8.00e+16 ohm-cm	8.00e+16 ohm-cm	IEC 60093
Dielectric Constant	3.3 @Frequency 5000 Hz	3.3 @Frequency 5000 Hz	60% RH; IEC 60250
	3.3 @Frequency 1000 Hz	3.3 @Frequency 1000 Hz	60% RH; IEC 60250
Dielectric Strength	17.0 kV/mm	432 kV/in	IEC 60243-1
Dissipation Factor	0.0020 @Frequency 5000 Hz	0.0020 @Frequency 5000 Hz	60% RH; IEC 60250
	0.020 @Frequency 1000 Hz	0.020 @Frequency 1000 Hz	60% RH; IEC 60250
Arc Resistance	144 sec	144 sec	W electrode; IEC 60950
CTE, linear, Parallel to Flow	110 µm/m-°C @Temperature -30.0 - 100 °C	61.1 µin/in-°F @Temperature -22.0 - 212 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	140 °C	284 °F	ISO 75-1,2
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ISO 75-1,2
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in