DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610 (Unverified Data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.08 g/cc0.0390 lb/in³DAM; ISO 1183吸水率3.3 %

@Thickness 2.00 mm

3.3 %

@Thickness 0.0787 in

DAM; Sim. to ISO 62水分吸收1.40 %

@Thickness 2.00 mm

1.40 %

@Thickness 0.0787 in

DAM; Sim. to ISO 62饱和吸水率0.58 %0.58 %DAM; Immersion 24h; ASTM D570粘度测试170 cm³/g170 cm³/gDAM; ISO 307 1157 1628线性成型收缩率,Flow0.012 cm/cm0.012 in/inDAM; ISO 294-4 2577线性成型收缩率，横向0.012 cm/cm0.012 in/inDAM; ISO 294-4 2577机械性能额定值 (公制)额定值 (英制)测试方法抗张强度2.87 MPa

@Strain 0.720 %, Temperature 90.0 °C

416 psi

@Strain 0.720 %, Temperature 194 °F

50%RH; ISO 11403-1 -2
2.91 MPa

@Strain 1.12 %, Temperature 150 °C

422 psi

@Strain 1.12 %, Temperature 302 °F

DAM; ISO 11403-1 -2
3.42 MPa

@Strain 0.240 %, Temperature 23.0 °C

496 psi

@Strain 0.240 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
3.52 MPa

@Strain 0.150 %, Temperature 23.0 °C

511 psi

@Strain 0.150 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
4.49 MPa

@Strain 0.180 %, Temperature 0.000 °C

651 psi

@Strain 0.180 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
5.82 MPa

@Strain 0.230 %, Temperature -20.0 °C

844 psi

@Strain 0.230 %, Temperature -4.00 °F

50%RH; ISO 11403-1 -2
5.87 MPa

@Strain 0.230 %, Temperature -40.0 °C

851 psi

@Strain 0.230 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
6.82 MPa

@Strain 0.250 %, Temperature 0.000 °C

989 psi

@Strain 0.250 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
7.64 MPa

@Strain 4.83 %, Temperature 150 °C

1110 psi

@Strain 4.83 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
8.73 MPa

@Strain 2.34 %, Temperature 90.0 °C

1270 psi

@Strain 2.34 %, Temperature 194 °F

DAM; ISO 11403-1 -2
11.24 MPa

@Strain 1.36 %, Temperature 40.0 °C

1630 psi

@Strain 1.36 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
14.82 MPa

@Strain 0.560 %, Temperature -20.0 °C

2149 psi

@Strain 0.560 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
16.03 MPa

@Strain 48.0 %, Temperature 150 °C

2325 psi

@Strain 48.0 %, Temperature 302 °F

DAM; ISO 11403-1 -2
23.07 MPa

@Strain 45.7 %, Temperature 90.0 °C

3346 psi

@Strain 45.7 %, Temperature 194 °F

50%RH; ISO 11403-1 -2
25.82 MPa

@Strain 47.28 %, Temperature 90.0 °C

3745 psi

@Strain 47.28 %, Temperature 194 °F

DAM; ISO 11403-1 -2
26.86 MPa

@Strain 1.18 %, Temperature -40.0 °C

3896 psi

@Strain 1.18 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
32.38 MPa

@Strain 11.02 %, Temperature 40.0 °C

4696 psi

@Strain 11.02 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
36.08 MPa

@Strain 22.41 %, Temperature 40.0 °C

5233 psi

@Strain 22.41 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
42.28 MPa

@Strain 9.84 %, Temperature 40.0 °C

6132 psi

@Strain 9.84 %, Temperature 104 °F

DAM; ISO 11403-1 -2
43.06 MPa

@Strain 8.32 %, Temperature 23.0 °C

6245 psi

@Strain 8.32 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
44.96 MPa

@Strain 20.95 %, Temperature 40.0 °C

6521 psi

@Strain 20.95 %, Temperature 104 °F

DAM; ISO 11403-1 -2
47.6 MPa

@Strain 18.65 %, Temperature 23.0 °C

6900 psi

@Strain 18.65 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
59.36 MPa

@Strain 3.41 %, Temperature 23.0 °C

8609 psi

@Strain 3.41 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
65.29 MPa

@Strain 8.78 %, Temperature 0.000 °C

9470 psi

@Strain 8.78 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
65.3 MPa

@Strain 3.17 %, Temperature -40.0 °C

9470 psi

@Strain 3.17 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
66.8 MPa

@Strain 3.56 %, Temperature 0.000 °C

9690 psi

@Strain 3.56 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
70.39 MPa

@Strain 3.61 %, Temperature -40.0 °C

10210 psi

@Strain 3.61 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
73.17 MPa

@Strain 4.99 %, Temperature -20.0 °C

10610 psi

@Strain 4.99 %, Temperature -4.00 °F

50%RH; ISO 11403-1 -2
80.89 MPa

@Strain 4.84 %, Temperature -20.0 °C

11730 psi

@Strain 4.84 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
89.79 MPa

@Strain 7.45 %, Temperature -40.0 °C

13020 psi

@Strain 7.45 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
90.45 MPa

@Strain 6.44 %, Temperature -40.0 °C

13120 psi

@Strain 6.44 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2拉伸模量1.20 GPa174 ksi50%RH; ISO 527-1/-2
2.30 GPa334 ksiDAM; ISO 527-1/-2弯曲强度86.0 MPa12500 psiDAM; ISO 178弯曲模量1.90 GPa276 ksiDAM; ISO 178割线模量0.137 GPa

@Strain 26.58 %, Temperature 40.0 °C

19.8 ksi

@Strain 26.58 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
0.214 GPa

@Strain 22.41 %, Temperature 23.0 °C

31.0 ksi

@Strain 22.41 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
0.215 GPa

@Strain 20.95 %, Temperature 40.0 °C

31.1 ksi

@Strain 20.95 %, Temperature 104 °F

DAM; ISO 11403-1 -2
0.294 GPa

@Strain 11.02 %, Temperature 40.0 °C

42.6 ksi

@Strain 11.02 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
0.430 GPa

@Strain 9.84 %, Temperature 40.0 °C

62.3 ksi

@Strain 9.84 %, Temperature 104 °F

DAM; ISO 11403-1 -2
0.518 GPa

@Strain 8.32 %, Temperature 23.0 °C

75.1 ksi

@Strain 8.32 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
0.744 GPa

@Strain 8.78 %, Temperature 0.000 °C

108 ksi

@Strain 8.78 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
0.826 GPa

@Strain 1.36 %, Temperature 40.0 °C

120 ksi

@Strain 1.36 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
0.988 GPa

@Strain 9.24 %, Temperature -40.0 °C

143 ksi

@Strain 9.24 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
1.21 GPa

@Strain 7.63 %, Temperature -40.0 °C

175 ksi

@Strain 7.63 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
1.425 GPa

@Strain 0.240 %, Temperature 23.0 °C

206.7 ksi

@Strain 0.240 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
1.47 GPa

@Strain 4.99 %, Temperature -20.0 °C

213 ksi

@Strain 4.99 %, Temperature -4.00 °F

50%RH; ISO 11403-1 -2
1.67 GPa

@Strain 4.84 %, Temperature -20.0 °C

242 ksi

@Strain 4.84 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
1.74 GPa

@Strain 3.41 %, Temperature 23.0 °C

252 ksi

@Strain 3.41 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
1.8764 GPa

@Strain 3.56 %, Temperature 0.000 °C

272.15 ksi

@Strain 3.56 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
1.95 GPa

@Strain 3.61 %, Temperature -40.0 °C

283 ksi

@Strain 3.61 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
2.06 GPa

@Strain 3.17 %, Temperature -40.0 °C

299 ksi

@Strain 3.17 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
2.28 GPa

@Strain 1.18 %, Temperature -40.0 °C

330 ksi

@Strain 1.18 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
2.35 GPa

@Strain 0.150 %, Temperature 23.0 °C

340 ksi

@Strain 0.150 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
2.49 GPa

@Strain 0.180 %, Temperature 0.000 °C

362 ksi

@Strain 0.180 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
2.53 GPa

@Strain 0.230 %, Temperature -20.0 °C

367 ksi

@Strain 0.230 %, Temperature -4.00 °F

50%RH; ISO 11403-1 -2
2.55 GPa

@Strain 0.230 %, Temperature -40.0 °C

370 ksi

@Strain 0.230 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
2.65 GPa

@Strain 0.560 %, Temperature -20.0 °C

384 ksi

@Strain 0.560 %, Temperature -4.00 °F

DAM; ISO 11403-1