DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer 物性表
比重 | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
密度 | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
Water Absorption | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Immersion 24h; ASTM D570 |
1.0 % @Temperature 23.0 °C | 1.0 % @Temperature 73.4 °F | Saturation, immersed; ISO 62, Similar to | |
线性成型收缩率 | 0.017 - 0.020 cm/cm @Thickness 3.20 mm | 0.017 - 0.020 in/in @Thickness 0.126 in | Transverse, 24h; ASTM D955 |
0.018 - 0.021 cm/cm @Thickness 3.20 mm | 0.018 - 0.021 in/in @Thickness 0.126 in | Flow, 24h; ASTM D955 | |
线性模具收缩,Flow | 0.018 - 0.021 cm/cm @Thickness 4.00 mm | 0.018 - 0.021 in/in @Thickness 0.157 in | Parallel, 24h; ISO 294-4 |
0.021 cm/cm @Thickness 2.00 mm | 0.021 in/in @Thickness 0.0787 in | ISO 294-4 | |
线性成型收缩率,横向 | 0.019 cm/cm @Thickness 2.00 mm | 0.019 in/in @Thickness 0.0787 in | ISO 294-4 |
0.018 - 0.021 cm/cm @Thickness 4.00 mm | Normal, 24h; ISO 294-4 | ||
熔体流动速率 | 1.0 g/10 min @Load 1.05 kg, Temperature 190 °C | 1.0 g/10 min @Load 2.31 lb, Temperature 374 °F | ASTM D1238 |
2.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | |
化合物熔体指数 | 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 374 °F | cm3/10 min; ISO 1133 |