Escorene™ Ultra FL 00209 物性表
物理性能额定值单位制测试方法
熔流率(熔体流动速率) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
醋酸乙烯含量 | 9.4 | wt% | ExxonMobil Method |
硬度额定值单位制测试方法
肖氏硬度 (邵氏 A, 15 秒) | 94 |
| ASTM D2240 |
机械性能额定值单位制测试方法
拉伸模量 1 | 110 | MPa | ASTM D638 |
伸长率 2(断裂) |
| % | ASTM D638 |
薄膜额定值单位制测试方法
割线模量 |
|
| ASTM D882 |
1% 正割, MD | 100 | MPa | ASTM D882 |
1% 正割, TD | 100 | MPa | ASTM D882 |
抗张强度 |
|
| ASTM D882 |
MD : 断裂 | 30.0 | MPa | ASTM D882 |
TD : 断裂 | 26.0 | MPa | ASTM D882 |
伸长率 |
|
| ASTM D882 |
MD : 断裂 | 510 | % | ASTM D882 |
TD : 断裂 | 650 | % | ASTM D882 |
落锤冲击 | 370 | g | ASTM D1709A |
埃尔曼多夫抗撕强度 |
|
| ASTM D1922 |
MD | 110 | g | ASTM D1922 |
TD | 170 | g | ASTM D1922 |
热性能额定值单位制测试方法
维卡软化温度 | 78.0 | °C | ASTM D1525 |