瑞士EMS增韧级PA12 Grilamid L25 W10 HX

Molding Shrinkage

Across Flow

1.2

%

Flow

0.80

Water Absorption

Saturation, 23°C

1.5

Equilibrium, 23°C, 50% RH

0.70

Dry

Conditioned

Unit

Test Method

Shore Hardness (Shore D, 15 sec)

67

Tensile Modulus

600

MPa

Tensile Stress

Yield

35.0

Break

40.0

Tensile Strain

15

> 50

Nominal Tensile Strain at Break

Dry

Charpy Notched Impact Strength

-30°C

7.0

kJ/m²

23°C

95

Charpy Unnotched Impact Strength

-30°C

No Break

23°C

Heat Deflection Temperature

0.45 MPa, Unannealed

115

°C

1.8 MPa, Unannealed

45.0

Continuous Use Temperature

-- 2

80.0 to 120

-- 3

150

Melting Temperature 4

175

CLTE

Flow

1.3E-4

cm/cm/°C

Transverse

1.6E-4

Surface Resistivity

1.0E+12

ohms

Volume Resistivity

1.0E+13

ohms·cm

Electric Strength

32

kV/mm

Comparative Tracking Index

V

Dry

Flammability Classification (0.8 mm)

HB