沙比克PPO NORYL PX1005X
SABIC Innovative Plastics NORYL PX1005X PPE+PS 物性表
| 比重 | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| 熔体流动速率 | 37 g/10 min @Load 5.00 kg, Temperature 280 °C | 37 g/10 min @Load 11.0 lb, Temperature 536 °F | ASTM D1238 |
| 化合物熔体指数 | 37 g/10 min @Load 5.00 kg, Temperature 280 °C | MVR [cm^3/10 min]; ISO 1133 |
| 抗张强度(断裂) | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 12.5 % | 12.5 % | 50 mm/min; ISO 527 |
| 17 % | 17 % | Type I, 50 mm/min; ASTM D638 | |
| 屈服伸长率 | 2.8 % | 2.8 % | 50 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.40 GPa | 348 ksi | 50 mm/min; ASTM D638 |
| 2.46 GPa | 357 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| 79.0 MPa | 11500 psi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.20 GPa | 319 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 2.43 GPa | 352 ksi | ASTM D790 | |
| 2.48 GPa | 360 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 3.00 J/cm | 5.62 ft-lb/in | ASTM D256 |
| 0.900 J/cm @Temperature -30.0 °C | 1.69 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 悬壁梁无缺口冲击强度 | 11.74 J/cm | 21.99 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| 简支梁缺口冲击强度 | 2.30 J/cm² | 10.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 体积电阻率 | 3.30e+16 ohm-cm | 3.30e+16 ohm-cm | ASTM D257 |
| 表面电阻 | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 |
| 介电常数 | 2.53 @Frequency 1.00e+6 Hz | 2.53 @Frequency 1.00e+6 Hz | ASTM D150 |
| 2.67 @Frequency 50.0 - 60.0 Hz | 2.67 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 介电强度 | 17.7 kV/mm @Thickness 3.20 mm | 450 kV/in @Thickness 0.126 in | in oil; ASTM D149 |
| 耗散因数 | 0.0026 @Frequency 1.00e+6 Hz | 0.0026 @Frequency 1.00e+6 Hz | ASTM D150 |
| 0.012 @Frequency 50.0 - 60.0 Hz | 0.012 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 耐电弧性 | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| 线形热膨胀系数 - 流动 | 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 49.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 线性热膨胀系数,横向流动 | 103 µm/m-°C @Temperature -40.0 - 40.0 °C | 57.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 载荷下热变形温度(0.46 MPa) | 88.0 °C | 190 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 84.0 °C @Thickness 3.20 mm | 183 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 88.0 °C @Thickness 6.40 mm | 190 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 75.0 °C | 167 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 72.0 °C @Thickness 3.20 mm | 162 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 78.0 °C @Thickness 6.40 mm | 172 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 94.0 °C | 201 °F | Rate B/50; ISO 306 |
| 97.0 °C | 207 °F | Rate B/120; ISO 306 | |
| 107 °C | 225 °F | Rate B/50; ASTM D1525 | |
| UL RTI | 95.0 °C | 203 °F | UL 746B |
| UL RTI，机械冲击 | 80.0 °C | 176 °F | UL 746B |
| UL RTI，机械无冲击 | 95.0 °C | 203 °F | UL 746B |
| 可燃性(UL94) | HB @Thickness 1.01 mm | HB @Thickness 0.0398 in | UL 94 |
| V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | UL 94 | |
| 5VA @Thickness 2.99 mm | 5VA @Thickness 0.118 in | UL 94 |