巴斯夫双6A3HG7巴斯夫双6 A3HG7

Physical PropertiesMetricEnglishCommentsDensity 1.41 g/cc0.0509 lb/in³ISO 1183Water Absorption 4.7 - 5.3 %4.7 - 5.3 %ISO 62Moisture Absorption at Equilibrium 1.4 - 1.8 %1.4 - 1.8 %23°C/50% R.H.; ISO 62Viscosity Number 140 cm³/g1.40 dl/gISO 307Linear Mold Shrinkage 0.0050 cm/cm0.0050 in/in
Melt Flow 56.4 g/10 min
@Load 5.00 kg,
Temperature 275 °C56.4 g/10 min
@Load 11.0 lb,
Temperature 527 °FISO 1133
Mechanical PropertiesMetricEnglishCommentsTensile Strength, Yield 200 MPa29000 psi50mm/min; ISO 527Elongation at Yield 3.0 %3.0 %50mm/min; ISO 527Modulus of Elasticity 11.2 GPa1620 ksiISO 527Flexural Strength 207 MPa30000 psiISO 178Flexural Modulus 10.0 GPa1450 ksiISO 178Izod Impact, Notched (ISO) 14.0 kJ/m²6.66 ft-lb/in²ISO 180/ACharpy Impact Unnotched 9.50 J/cm²45.2 ft-lb/in²ISO 179/1eU 7.50 J/cm²
@Temperature -30.0 °C35.7 ft-lb/in²
@Temperature -22.0 °FISO 179/1eUCharpy Impact, Notched 1.30 J/cm²6.19 ft-lb/in²ISO 179/1eA 1.20 J/cm²
@Temperature -30.0 °C5.71 ft-lb/in²
@Temperature -22.0 °FISO 179/1eA
Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+15 ohm-cm1.00e+15 ohm-cmIEC 60093Dielectric Constant 3.5
@Frequency 1.00e+6 Hz3.5
@Frequency 1.00e+6 HzIEC 60250Dissipation Factor 0.020
@Frequency 1.00e+6 Hz0.020
@Frequency 1.00e+6 HzIEC 60250Comparative Tracking Index 550 V550 VTest Solution A; IEC 60112
Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 15.0 - 20.0 µm/m-°C
@Temperature 23.0 - 80.0 °C8.33 - 11.1 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-1/-2CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C33.3 - 38.9 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-1/-2Specific Heat Capacity 1.50 J/g-°C0.359 BTU/lb-°F
Thermal Conductivity 0.350 W/m-K2.43 BTU-in/hr-ft²-°FDIN 52612Melting Point 260 °C500 °FDIN 53765Maximum Service Temperature, Air 140 °C284 °Ffor 50% loss of tensile strength after 20,000 hr
170 °C338 °Ffor 50% loss of tensile strength after 5,000 hr
240 °C464 °F
Deflection Temperature at 0.46 MPa (66 psi) 250 °C482 °FISO 75Deflection Temperature at 1.8 MPa (264 psi) 250 °C482 °FISO 75Flammability, UL94 HB
@Thickness 1.60 mmHB
@Thickness 0.0630 in