DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data)
Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 40% Mineral FilledDuPont Performance PolymersDuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**) 物性表
| 密度 | 1.50 g/cc | 0.0542 lb/in³ | DAM; ISO 1183 |
| 填料含量 | 40 % | 40 % | DAM |
| Water Absorption | 1.6 % @Temperature 23.0 °C | 1.6 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to |
| 抗张强度(断裂) | 54.0 MPa @Temperature 23.0 °C | 7830 psi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 82.0 MPa @Temperature 23.0 °C | 11900 psi @Temperature 73.4 °F | DAM; ISO 527 | |
| 伸长率 (断裂) | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 |
| 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |
| 拉伸模量 | 3.80 GPa @Temperature 23.0 °C | 551 ksi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 6.60 GPa @Temperature 23.0 °C | 957 ksi @Temperature 73.4 °F | DAM; ISO 527 | |
| 悬壁梁缺口冲击强度 | 3.50 kJ/m² @Temperature 23.0 °C | 1.67 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |
| 简支梁无缺口冲击强度 | 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.350 J/cm² @Temperature 23.0 °C | DAM; ISO 179/1eA | |
| 0.450 J/cm² @Temperature 23.0 °C | 2.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA |
| 相比耐漏电起痕指数(CTI) | >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A |
| 熔融温度 | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 240 °C | 464 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 170 °C | 338 °F | DAM; ISO 75-1/-2 |
| UL RTI | 105 °C @Thickness 0.710 mm | 221 °F @Thickness 0.0280 in | DAM; UL 746B |
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |
| UL RTI，机械冲击 | 65.0 °C @Thickness 0.710 mm | 149 °F @Thickness 0.0280 in | DAM; UL 746B |
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |
| 115 °C @Thickness 3.00 mm | 239 °F @Thickness 0.118 in | DAM; UL 746B | |
| UL RTI，机械无冲击 | 65.0 °C @Thickness 0.710 mm | DAM; UL 746B | |
| 115 °C @Thickness 1.50 mm | 239 °F @Thickness 0.0591 in | DAM; UL 746B | |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 |
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.710 mm | DAM; IEC 60695-11-10 |
| 加工（熔体）温度 | 285 - 305 °C | 545 - 581 °F | DAM |
| 295 °C | 563 °F | DAM; Optimum | |
| 模具温度 | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | <= 0.20 % | <= 0.20 % | DAM |
| 外观 | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Mineral filler | DAM |
| 形式 | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | >PA66-MD40< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Low Warp Resins | DAM |
| Mineral Reinforced Resins | DAM | |
| Mineral Reinforced Resins | DAM | |
| 树脂识别 | PA66-MD40 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |