德国巴斯夫A3HG3德国巴斯夫A3HG3英文溶化体积流率
Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
Water Absorption | 7.0 % | 7.0 % | ISO 62 |
Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 |
Viscosity Number | 140 cm³/g | 1.40 dl/g | |
Melt Flow | 70 g/10 min @Temperature 275 °C | 70 g/10 min @Temperature 527 °F | ISO 1133 |
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
Tensile Modulus | 6.00 GPa | 870 ksi | 1mm/min; ISO 527 |
Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179 |
4.30 J/cm² @Temperature -30.0 °C | 20.5 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |
Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 |
Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 |
0.014 @Frequency 100 Hz | 0.014 @Frequency 100 Hz | IEC 60250 | |
Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
CTE, linear, Parallel to Flow | 33.0 µm/m-°C | 18.3 µin/in-°F | ISO 11359 |
CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359 |
Melting Point | 260 °C | 500 °F | 10 K/min |
Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
Vicat Softening Point | 250 °C | 482 °F | (50 °C/h / 50N) - B/50; ISO 306 |
Flammability, UL94 | HB @Thickness 1.65 mm | HB @Thickness 0.0650 in | |
HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||
Oxygen Index | 24 % | 24 % | ISO 4589-1/-2 |