上海巴斯夫A3X2G7巴斯夫A3X2G7英文物性
Physical PropertiesMetricEnglishCommentsDensity 1.45 g/cc0.0524 lb/in³ISO 1183Water Absorption 4.4 - 5.0 %4.4 - 5.0 %ISO 62Moisture Absorption at Equilibrium 1.0 - 1.4 %1.0 - 1.4 %23°C/50% R.H.; ISO 62Viscosity Number 140 cm³/g1.40 dl/gISO 307Linear Mold Shrinkage 0.0045 cm/cm0.0045 in/in
Melt Flow 43.5 g/10 min
@Load 5.00 kg,
Temperature 275 °C43.5 g/10 min
@Load 11.0 lb,
Temperature 527 °FISO 1133
Mechanical PropertiesMetricEnglishCommentsTensile Strength, Yield 160 MPa23200 psi50mm/min; ISO 527Elongation at Yield 3.0 %3.0 %50mm/min; ISO 527Modulus of Elasticity 11.0 GPa1600 ksiISO 527Flexural Modulus 9.20 GPa1330 ksiISO 178Izod Impact, Notched (ISO) 13.0 kJ/m²6.19 ft-lb/in²ISO 180/ACharpy Impact Unnotched 7.00 J/cm²33.3 ft-lb/in²ISO 179/1eU 6.50 J/cm²
@Temperature -30.0 °C30.9 ft-lb/in²
@Temperature -22.0 °FISO 179/1eUCharpy Impact, Notched 1.40 J/cm²6.66 ft-lb/in²ISO 179/1eA 10.00 J/cm²
@Temperature -30.0 °C47.59 ft-lb/in²
@Temperature -22.0 °FISO 179/1eA
Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+13 ohm-cm1.00e+13 ohm-cmIEC 60093Dielectric Constant 3.6
@Frequency 1.00e+6 Hz3.6
@Frequency 1.00e+6 HzIEC 60250Dissipation Factor 0.020
@Frequency 1.00e+6 Hz0.020
@Frequency 1.00e+6 HzIEC 60250Comparative Tracking Index 600 V600 VTest Solution A; IEC 60112
Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 15.0 - 20.0 µm/m-°C
@Temperature 23.0 - 80.0 °C8.33 - 11.1 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-1/-2CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C33.3 - 38.9 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-1/-2Specific Heat Capacity 1.40 J/g-°C0.335 BTU/lb-°F
Thermal Conductivity 0.340 W/m-K2.36 BTU-in/hr-ft²-°FDIN 52612Melting Point 260 °C500 °FDIN 53765Maximum Service Temperature, Air 140 °C284 °Ffor 50% loss of tensile strength after 20,000 hr
157 °C315 °Ffor 50% loss of tensile strength after 5,000 hr
220 °C428 °F
Deflection Temperature at 0.46 MPa (66 psi) 250 °C482 °FISO 75Deflection Temperature at 1.8 MPa (264 psi) 250 °C482 °FISO 75Flammability, UL94 HB
@Thickness >=0.400 mmHB
@Thickness >=0.0157 in
V-0
@Thickness >=0.750 mmV-0
@Thickness >=0.0295 in