Physical PropertiesMetricEnglishCommentsDensity 1.32 g/cc0.0477 lb/in³ISO 1183Water Absorption 5.7 - 6.3 %5.7 - 6.3 %ISO 62Moisture Absorption at Equilibrium 1.7 - 2.1 %1.7 - 2.1 %23°C/50% R.H.; ISO 62Viscosity Number 145 cm³/g1.45 dl/gISO 307Linear Mold Shrinkage 0.0055 cm/cm0.0055 in/in
Melt Flow 66 g/10 min
@Load 5.00 kg,
Temperature 275 °C66 g/10 min
@Load 11.0 lb,
Temperature 527 °FISO 1133
Mechanical PropertiesMetricEnglishCommentsTensile Strength, Yield 180 MPa26100 psiISO 527Elongation at Yield 3.0 %3.0 %ISO 527Modulus of Elasticity 8.60 GPa1250 ksiISO 527Flexural Strength 260 MPa37700 psiISO 178Flexural Modulus 7.60 GPa1100 ksiISO 178Izod Impact, Notched (ISO) 9.50 kJ/m²4.52 ft-lb/in²ISO 180/aCharpy Impact Unnotched 6.50 J/cm²30.9 ft-lb/in²ISO 179/1eU 5.50 J/cm²
@Temperature -30.0 °C26.2 ft-lb/in²
@Temperature -22.0 °FISO 179/1eUCharpy Impact, Notched 1.20 J/cm²5.71 ft-lb/in²ISO 179/1eA 0.900 J/cm²
@Temperature -30.0 °C4.28 ft-lb/in²
@Temperature -22.0 °FISO 179/1eA
Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+13 ohm-cm1.00e+13 ohm-cmIEC 60093Dielectric Constant 3.5
@Frequency 1.00e+6 Hz3.5
@Frequency 1.00e+6 HzIEC 60250Dissipation Factor  0.014
@Frequency 1.00e+6 Hz0.014
@Frequency 1.00e+6 HzIEC 60250
0.014
@Frequency 100 Hz0.014
@Frequency 100 HzIEC 60250Comparative Tracking Index 450 V450 VIEC 60112
Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 25.0 - 35.0 µm/m-°C
@Temperature 23.0 - 80.0 °C13.9 - 19.4 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C33.3 - 38.9 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359Specific Heat Capacity 1.60 J/g-°C0.382 BTU/lb-°F
Thermal Conductivity 0.340 W/m-K2.36 BTU-in/hr-ft²-°FDIN 52612Melting Point 260 °C500 °FDIN 53765Maximum Service Temperature, Air 145 °C293 °Ffor 50% loss of tensile strength after 20,000 hr
175 °C347 °Ffor 50% loss of tensile strength after 5,000 hr
240 °C464 °F
Deflection Temperature at 0.46 MPa (66 psi) 250 °C482 °FISO 75Deflection Temperature at 1.8 MPa (264 psi) 245 °C473 °FISO 75Flammability, UL94 HB
@Thickness 1.60 mmHB
@Thickness 0.0630 in