Physical PropertiesMetricEnglishCommentsMechanical PropertiesMetricEnglishCommentsElectrical PropertiesMetricEnglishComments

Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.39 g/cc	0.0502 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	1.1 - 1.5 %	1.1 - 1.5 %	ISO 62
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in
Melt Flow	34.75 g/10 min @Load 5.00 kg, Temperature 275 °C	34.75 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Tensile Strength at Break	145 MPa	21000 psi	ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	ISO 527-1/-2
Modulus of Elasticity	9.50 GPa	1380 ksi	ISO 527-1/-2
Flexural Strength	230 MPa	33400 psi	ISO 178
Flexural Modulus	9.50 GPa	1380 ksi	ISO 178
Charpy Impact Unnotched	6.30 J/cm² @Temperature -30.0 °C	30.0 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	6.50 J/cm² @Temperature 23.0 °C	30.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.750 J/cm² @Temperature 23.0 °C	3.57 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.017 @Frequency 1.00e+6 Hz	0.017 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Solution A; IEC 60112
Hot Wire Ignition, HWI	0.00 sec @Thickness >=0.750 mm	0.00 sec @Thickness >=0.0295 in	ASTM D 3874-88
High Amp Arc Ignition, HAI	0.00 arcs @Thickness >=0.750 mm	0.00 arcs @Thickness >=0.0295 in	US 746C