尼龙66 A3UG5尼龙66 A3UG5
Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | ISO 62 |
Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
Melt Flow | 34.75 g/10 min @Load 5.00 kg, Temperature 275 °C | 34.75 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 |
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 |
Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
Modulus of Elasticity | 9.50 GPa | 1380 ksi | ISO 527-1/-2 |
Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
Charpy Impact Unnotched | 6.30 J/cm² @Temperature -30.0 °C | 30.0 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU |
6.50 J/cm² @Temperature 23.0 °C | 30.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |
Charpy Impact, Notched | 0.750 J/cm² @Temperature 23.0 °C | 3.57 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 |
Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 |
Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
Hot Wire Ignition, HWI | 0.00 sec @Thickness >=0.750 mm | 0.00 sec @Thickness >=0.0295 in | ASTM D 3874-88 |
High Amp Arc Ignition, HAI | 0.00 arcs @Thickness >=0.750 mm | 0.00 arcs @Thickness >=0.0295 in | US 746C |
填料/增强材料 | 玻璃纤维增强材料, 25% 填料按重量 |
添加剂 | 阻燃性 |
特性 | 良好的电气性能 磷含量,低(到无) 无卤 阻燃性 |
机构评级 | EC 1907/2006 (REACH) |